ORNL scientist Adrian Sabau describes components of a laser-interference structuring system that was used to treat aluminum alloy sheets for corrosion protection. (Photo courtesy Carlos Jones/ORNL, U.S. Dept. of Energy)

A novel application of a laser-interference structuring technique answers a call from the U.S. DoD to explore nonchemical alternatives for corrosion protection in military vehicles and aircraft systems.

 Contributed by Oak Ridge National Laboratory

Long-lasting protection from corrosion is essential for materials used for vehicles and aircraft to ensure structural integrity amid extreme operating conditions. Two chemical pre-treatment processes are widely used in industrial settings to prepare for coating adhesion and protect aluminum alloy surfaces against corrosion. While highly regulated, both processes use large quantities of hazardous compounds with known environmental and health risks.

A multidisciplinary team of scientists at the Department of Energy’s Oak Ridge National Laboratory has applied a laser-interference structuring, or LIS, technique that makes significant strides toward eliminating the need for these hazardous chemicals. The novel application of the LIS method answers a call from the U.S. Department of Defense for research projects that explore nonchemical alternatives for corrosion protection in military vehicles and aircraft systems.

Chromate conversion coating, or CCC, uses hexavalent chromium, a known carcinogen, to inhibit corrosion. Sulfuric acid anodizing (SAA) uses sulfuric acid, which can severely irritate skin and eyes, and, when inhaled, can lead to permanent lung damage. Millions of gallons of used chemical solutions are disposed of annually as hazardous waste.

DoD owns and operates hundreds of industrial facilities that manufacture and repair the vehicles and equipment it operates, spending more than $20 billion in corrosion protection annually.

The military operates more than 12,000 aircraft, 10,000 tanks, hundreds of ships, and a multitude of other vehicles and weapons systems. The DoD owns and operates hundreds of industrial facilities that manufacture and repair these vehicles and equipment, spending more than $20 billion in corrosion protection annually.

The agency’s Strategic Environmental Research and Development Program, or SERDP, planned and executed with the Department of Energy and the Environmental Protection Agency, is “focused on developing alternative technologies to eliminate materials and processes that are of environmental concern,” said Robin Nissan, program manager of SERDP and its sister program, the Environmental Security Technology Certification Program.

Adrian Sabau holds a primer-coated specimen, which was pretreated with a laser-interference structuring technique and shows coating adhesion. (Photo courtesy of Carlos Jones/ORNL, U.S. Dept. of Energy)

“Our defense systems require repair and refurbishment,” he said. “Our programs are investing in the development of alternative processes that can ensure robust performance, sustainable practices, and eliminate environmental risk.”

In three successive publications, ORNL materials scientist Adrian Sabau and a team of chemists and manufacturing scientists described, demonstrated, and analyzed an LIS technique and compared its performance to the traditional solvent-intensive methods. Co-authors on the research included ORNL’s Jiheon Jun, Mike Stephens, Dana McClurg, Harry Meyer III, Donovan Leonard, and Jian Chen.

Sabau, who specializes in materials processing such as metal casting and solidification, and his team had recently completed a project using LIS for bonding in automotive applications. He recognized that a similar technique could be effective for coating adhesion as well.

Sabau, who specializes in materials processing such as metal casting and solidification, and his team had recently completed a project using LIS for bonding in automotive applications. When he read DoD’s call for research on nonsolvent surface preparation, Sabau recognized that a similar technique could be effective for coating adhesion as well.

In their experiments, they treated aluminum alloy sheets by splitting the primary beam of a pulsed nanosecond laser into two beams and focusing them on the same spot on the specimen surface. This process roughened the surface with periodic structures, and changed the surface chemistry and sub-surface microstructure.

“In laser processing, you’re impacting lots of energy on the top surface, and we need to understand what’s happening to the substrate. Is it damaged? Does it crack? Are there any microstructure effects that are not beneficial to corrosion protection?”

“In laser processing, you’re impacting lots of energy on the top surface, and we need to understand what’s happening to the substrate. Is it damaged? Does it crack? Are there any microstructure effects that are not beneficial to corrosion protection?” Sabau said.

Adrian Sabau logs settings in a test of the laser-interference structuring system. Credit: Carlos Jones/ORNL, U.S. Dept. of Energy

Meyer, a physical chemist, and Leonard, a microscopist, contributed to the characterization work outlined in Optics and Laser Technology. Meyer conducted surface chemical analysis using X-ray photoelectron spectroscopy, or XPS.

“XPS is a material characterization technique that can determine what elements are on the surface — the top 5 to 8 nanometers — of solid materials,” Meyer said. “Before laser processing, XPS was used to determine the chemical composition of the as-received aluminum alloy sheets, which showed high amounts of carbon. XPS was used again to determine if the laser processing cleaned the surface.

“The results showed a significant reduction of the carbon, [which] was one of our key findings. XPS, along with electron microscopy results, helped us to understand how the native oxide was altered through laser processing.”

Sabau added, “In looking at subsurface characterization, we found a beneficial aspect that we bumped into by accident. In the top layer, we saw the dissolution of copper-rich precipitates, where corrosion can initiate.”

After an aluminum alloy sheet is cleaned, often the surface energy prohibits the coating from sticking properly, a known issue in industrial surface coatings.

After an aluminum alloy sheet is cleaned, often the surface energy prohibits the coating from sticking properly, a known issue in industrial surface coatings. The team’s next publication, for the International Journal of Adhesion and Adhesives, looked at coating adhesion and found that the LIS method provided adhesion as well as the industry-standard and solvent-intensive CCC and SAA techniques. A patent for coating adhesion was awarded in 2021 based on this LIS technique.

For the adhesion study, McClurg conducted profilometry on the materials, a technique that maps surface contours and provides roughness measurements.

A primer-coated specimen shows marks from the laser system. Credit: Carlos Jones/ORNL, U.S. Dept. of Energy

The third paper, published in Corrosion: The Journal of Science and Engineering, outlined the final tests that Sabau’s team conducted with an epoxy primer used by the U.S. military for airplane wings and bodies.

Technician Mike Stephens completed the delicate and time-sensitive task of applying spray coatings of primers and topcoats to exacting DoD specifications on alloy sheets that had been prepared with different treatments. He then exposed the samples to 2,000 hours of salt spray to examine corrosion resistance at multiple periods. Jun led the corrosion testing, investigating how the LIS-prepared surfaces compared to conventionally prepared alloy substrates, both with and without primer and a topcoat.

“The laser interference-treated substrate exhibited higher corrosion resistance,” said Jun, who attributed the result to copper-rich precipitates dissolving. However, on the samples coated with primer or primer and topcoat, LIS did not perform as well as the chemical solvent techniques, with some samples showing blisters within 96 hours of salt spray exposure. However, those blisters were small and remained stable through hundreds of hours of exposure.

The team tested a second set of samples that were simply wiped down with acetone prior to the application of primer, resulting in very little corrosion, and the formation of blisters was delayed by hundreds of hours.

Jun said further investigation to optimize LIS would be worthwhile.

“Our research approach, combining lab-scale electrochemical measurements and industrially adopted ASTM [American Society for Testing Materials] salt spray testing, was very successful and aided in-depth understanding of the effects of laser interference treatment,” he said.

“For a process that was conducted at ambient temperature without solvents, most of the samples performed extremely well,” Sabau said. “This technique is a huge step in the right direction towards nonchemical intensive surface preparation for coatings.”

“For a process that was conducted at ambient temperature without solvents, most of the samples performed extremely well,” Sabau said. “This technique is a huge step in the right direction towards nonchemical intensive surface preparation for coatings.”

Oak Ridge National Laboratory is managed by UT-Battelle for the Department of Energy’s Office of Science, the single largest supporter of basic research in the physical sciences in the United States. DOE’s Office of Science is working to address some of the most pressing challenges of our time.

For more information, please visit energy.gov/science.

Source: Oak Ridge National Laboratory

Subscribe Now

Design-2-Part Magazine

Get the manufacturing industry news and features you need for free in a format you like.

FREE Print, Digital, or Both »

You have Successfully Subscribed!